EN353 Bright Bar

EN353 – BRIGHT BAR Grade Introduction:

We are EN353 Steel Bright Round Bar manufacturers and we are manufacturing from prime quality billets and blooms. The range of EN353 Round Bars which we manufacture for our customers are of high quality and these round bars are used for making machinery and Auto components. These products have been made keeping in mind the quality parameters which have been set by the industry in the market. EN353 Round Bars are always supplied with the test certificates and can be supplied in bulk quantity as well as retail quantity as per customer’s requirements. EN353 alloy Steel round bars are supplied by us to various industries. EN353 is a very high strength steel alloy which is hardened and tempered before supplying and has nickel, chromium, molybdenum making it high tensile steel strength, with good ductility and wear resistance. With relatively good impact properties at low temperatures, EN353 is also suitable for a variety of elevated temperature applications. EN353 round bars have good internal strength and high external strength, which makes it highly wear resistant. EN353 steel round bars offer good combination of ductility, strength and wear resistance. EN353 is a very high strength alloy engineering steel.

EN353 – BRIGHT BAR Grade Application:

Acceptable for many automobile applications such as heavy duty gear, shaft, pinion, camshafts, gudgeon pins.

EN353 – BRIGHT BAR Equivalent grades:

BRITISH BS 970:1991 815M17 BRITISH BS 970:1955 EN353 GERMAN DIN 20NiCrMo5 FRENCH AFNOR 20NCD5 SWEDISH SS 2523 EUROPEAN STEEL NAME 17NiCrMoS6-4 EUROPEAN STANDARD EN10277-4

EN353 – BRIGHT BAR Chemical composition:

The following table shows the chemical composition of EN353 steel:

Element	C	Si	Mn	P	S	Cr	Mo	Ni
Content (%)	0.10-0.20	0.10-0.35	0.50-1.00	0.040 Max	0.040 Max	0.75-1.25	0.08-0.15	1.00-1.50

EN353 – BRIGHT BAR Mechanical Properties:

Mechanical Properties
Hardening	840-870
Queching	oil
Tempering	150-200
Brinell Rockwell Hardness	150-200

Other Details of Property

EN353 – BRIGHT BAR Hardness:

HB – 270 

EN353 – BRIGHT BAR Heat treatment:

The hardening treatment for most steels consists of heating the steel to a set temperature and then cooling it rapidly by plunging it into oil, water. EN8 and EN353 steel is an easily available and cheap material that is acceptable for heavy duty applications.

EN353 – BRIGHT BAR Hardening:

Hardening °C 780-820.

EN353 – BRIGHT BAR Tempering:

EN353 is re-heated  to 780C – 820°C, holding until  the temperature is uniform throughout the section, and then  quenched  in oil, Tempering must be done  immediately while  the component EN353 is still hand warm. Heat to 150C – 200°c , soak it  for 1 – 2 hours / 25mm of section, and then  cooled  in still air. Hardness after Tempering  : 62-64 HRC.

EN353 – BRIGHT BAR Physical Properties:

Thermal Conductivity at °C	20	350	700
W/(m*K)	11.3	13.3	14.5

EN353 – BRIGHT BAR Forging Properties:

EN353 steel round bars offer good combination of ductility, strength and wear resistance. EN353 is a very high strength alloy engineering steel.

EN353 – BRIGHT BAR Stress Reliving:

150-200, cooled in furnace.  1st pre-heating °Cup to approx. 400 in an air-circulating furnace 2nd and 3^rd : 780 and 805°C.

EN353 – BRIGHT BAR Annealing:

630-670°C

EN353 – BRIGHT BAR Density:

DENSITY (G/CM 3)	8.08
DENSITY (LB/IN 3)	0.292

EN353 – BRIGHT BAR Machinability:

75

EN353 – BRIGHT BAR  Welding:

Pre / post heat precaution required.